Lubrizol Pellethane® 2363-80A Thermoplastic Polyurethane Elastomer

Thermoplastic Polyurethane, Elastomer, Ether Grade

Lubrizol (former Noveon)

产品说明：

Features: USP Class VI

Available in Americas, Europe, Middle East, Africa, India and Asia

Data provided by Lubrizol

Lubrizol acquired the Pellethane product line from Dow in 2009.

物性信息：

物理性能额定值 (公制)额定值 (英制)测试方法

密度	1.13 g/cc	0.0408 lb/in³	ASTM D792
线性成型收缩率,Flow	0.0050 - 0.0080 cm/cm	0.0050 - 0.0080 in/in	ASTM D955
线性成型收缩率，横向	0.00 - 0.0040 cm/cm	0.00 - 0.0040 in/in	ASTM D955
熔体流动速率	23 g/10 min @Load 1.20 kg, Temperature 224 °C	23 g/10 min @Load 2.65 lb, Temperature 435 °F	ASTM D1238

机械性能额定值 (公制)额定值 (英制)测试方法

肖氏硬度 (邵氏 A)	81	81	ASTM D2240
极限抗拉强度	35.8 MPa	5190 psi	ASTM D412
伸长率 (断裂)	550 %	550 %	ASTM D412
50% Modulus	0.00410 GPa	0.595 ksi	ASTM D412
**** 模量	0.00610 GPa	0.885 ksi	ASTM D412
300％模量	0.0121 GPa	1.75 ksi	ASTM D412
撕裂强度	82.3 kN/m	470 pli	Die C; ASTM D624
泰伯磨损，毫克/1000次	20	20	H22 Wheel, 1000g; ASTM D1044
压缩**变形	25 % @Temperature 25.0 °C, Time 79200 sec	25 % @Temperature 77.0 °F, Time 22.0 hour	ASTM D395 Method B
	30 % @Temperature 70.0 °C, Time 79200 sec	30 % @Temperature 158 °F, Time 22.0 hour	ASTM D395 Method B
Tensile Set	30 %	30 %	Elongation set after break; ASTM D412

热性能额定值 (公制)额定值 (英制)测试方法

线性热膨胀系数	170 µm/m-°C @Temperature -80.0 - -30.0 °C	94.4 µin/in-°F @Temperature -.0 °F	ASTM D696
维卡软化温度	85.0 °C	185 °F	120°C/hr, 9.8N; ASTM D1525
玻璃化转变温度，Tg	-42.0 °C	-43.6 °F

加工性能额定值 (公制)额定值 (英制)测试方法

加工（熔体）温度	°C	°F	Molding
模具温度	16.0 - 60.0 °C	60.8 - 140 °F
干燥温度	82.0 - 93.0 °C	°F	air dew point <-40°C